Key |
Units Shown |
Alternate Units |
1 |
Density |
g / cm3 |
= 0.528 tz / in3 |
2 |
Young's Modulus |
GPa |
= 0.145x106 psi |
3 |
Yield Strength |
MPa |
= 0.145 kpsi |
4 |
Tensile Strength |
MPa |
= 0.145 kpsi |
5 |
Thermal Conductivity |
W/(m*K) |
= BTU/(h*ft*°F) |
6 |
Thermal Coefficient of Expansion |
x10-6 /°C |
= 0.556x10-6 /°F |
7 |
Electrical Resistivity |
x10-9 ohm*m |
|
8 |
Electrical Conductivity |
x106 / (ohm*m) |
|
9 |
Hardness |
KHN |
|
10 |
Elongation |
% |
|
Alloy |
1 |
2 |
3 |
4 |
5 |
6 |
7 |
8 |
9 |
10 |
35Au-65Cu |
11.0 |
|
107 |
328 |
90 |
19.1 |
85 |
11.8 |
|
27 |
37.5Au-62.5Cu |
11.1 |
|
72 |
379 |
83 |
18.8 |
93 |
10.8 |
|
30 |
40Au-60Cu |
11.4 |
|
69 |
427 |
75 |
18.6 |
103 |
9.7 |
|
33 |
50Ag-50Pd |
11.2 |
|
|
379 |
|
|
|
|
|
|
50Au-50Cu |
12.0 |
|
613 |
658 |
33 |
19.2 |
237 |
4.2 |
|
38 |
70Au-30Ni |
14.2 |
|
|
|
|
|
|
|
|
5 |
80Au-20Cu |
15.5 |
|
127 |
393 |
52.0 |
17.9 |
131 |
7.6 |
|
|
95Ag-5Al |
9.2 |
|
|
|
|
|
|
|
|
|
Cocuman |
8.0 |
|
|
|
|
|
|
|
|
|
Coin Silver |
10.3 |
|
280 |
|
|
|
|
|
|
32 |
Copper |
8.9 |
125 |
69 |
221 |
398.0 |
19.4 |
17 |
60.0 |
|
55 |
Copper ABA® |
8.1 |
96 |
279 |
520 |
38.0 |
19.5 |
198 |
5.1 |
110 |
42 |
Croniro® |
13.9 |
|
|
|
|
|
|
|
|
|
Cronisi® |
7.5 |
|
|
|
|
|
|
|
|
|
Cusil® |
10.0 |
83 |
272 |
372 |
371 |
19.6 |
20.4 |
49.0 |
101 |
19 |
Cusil-ABA® |
9.8 |
83 |
271 |
346 |
180.0 |
18.5 |
44 |
23.0 |
110 |
20 |
Cusiltin-10 |
9.75 |
|
358 |
462 |
30 |
|
247 |
4.0 |
|
38 |
Cusiltin-5 |
9.9 |
|
|
|
|
|
|
|
|
|
Cusin-1 ABA® |
9.7 |
83 |
260 |
402 |
170.0 |
18.7 |
46 |
22.0 |
110 |
22 |
Gapasil®-9 |
|
|
118 |
285 |
55.6 |
|
136 |
7.4 |
|
41 |
Gemco® |
8.8 |
|
117 |
306 |
24.3 |
|
311 |
3.2 |
|
450 |
Georo |
14.7 |
|
|
210 |
|
|
|
|
|
1 |
Gold-ABA® |
18.3 |
87 |
209 |
334 |
25.0 |
16.1 |
308 |
3.3 |
130 |
29 |
Incuro-60 |
13.0 |
|
305 |
517 |
47.0 |
|
163 |
6.1 |
|
37 |
Incusil®-10 |
9.8 |
81 |
345 |
420 |
85.0 |
19.6 |
90 |
11.1 |
118 |
19 |
Incusil®-15 |
9.8 |
76 |
386 |
448 |
55.0 |
18.5 |
141 |
7.1 |
125 |
19 |
Incusil® ABA® |
9.7 |
76 |
338 |
455 |
70.0 |
18.2 |
106 |
9.4 |
100 |
21 |
Nicoro® |
10.9 |
|
185 |
427 |
70.0 |
17.8 |
110 |
9.1 |
|
28 |
Nicoro®-80 |
15.6 |
|
372 |
520 |
50.0 |
17.8 |
153 |
6.5 |
|
22 |
Nicuman®-23 |
7.9 |
|
322 |
590 |
8.9 |
|
845 |
1.2 |
|
|
Nicuman®-37 |
7.7 |
|
305 |
595 |
10.4 |
|
732 |
1.4 |
|
|
Nicusil®-3 |
10.0 |
|
207 |
330 |
223.0 |
|
34 |
29.0 |
|
32 |
Nicusil®-8 |
|
|
339 |
366 |
237.0 |
|
32 |
31.3 |
|
20 |
Nioro® |
15.7 |
|
686 |
792 |
28.0 |
17.5 |
274 |
3.7 |
|
14 |
Palco |
10.4 |
|
341 |
661 |
35.0 |
|
219 |
4.6 |
|
43 |
Palcusil®-10 |
10.0 |
|
327 |
374 |
145.0 |
18.5 |
53 |
18.9 |
|
18 |
Palcusil®-15 |
10.3 |
|
379 |
448 |
98.0 |
|
78 |
13.0 |
|
23 |
Palcusil®-25 |
10.4 |
|
|
|
|
|
|
|
|
|
Palcusil®-5 |
10.0 |
|
333 |
380 |
208.0 |
17.2 |
37 |
27.0 |
|
11 |
Palni® |
10.4 |
|
772 |
978 |
42.0 |
15.0 |
184 |
5.4 |
|
23 |
Palnicro®-36-M |
8.8 |
|
|
|
|
|
|
|
|
|
Palnicurom®-10 |
10.5 |
132 |
411 |
770 |
12.5 |
18.8 |
606 |
165.0 |
212 |
31 |
Palnicusil® |
10.3 |
|
|
|
|
|
|
|
|
|
Palniro®-1 |
13.1 |
|
723 |
840 |
20.0 |
16.0 |
376 |
2.7 |
327 |
24 |
Palniro®-4 |
11.6 |
|
655 |
827 |
29.0 |
17.0 |
269 |
3.7 |
337 |
28 |
Palniro®-7 |
14.5 |
|
758 |
847 |
21.0 |
14.0 |
369 |
2.7 |
327 |
20 |
Palnisi-47 |
9.9 |
|
|
|
3.7 |
|
2 |
0.5 |
|
|
Paloro® |
18.4 |
|
110 |
198 |
105.0 |
|
73 |
13.7 |
|
23 |
Palsil®-10 |
10.6 |
|
95 |
205 |
108.0 |
|
70 |
14.0 |
|
40 |
RI-46 |
11.1 |
|
752 |
869 |
|
|
|
|
|
|
RI-48 |
9.5 |
|
|
|
|
|
|
|
|
|
RI-49 |
10.6 |
|
752 |
869 |
|
|
|
|
|
|
Silcoro-60 |
13.7 |
|
|
|
|
|
|
|
|
|
Silcoro-75 |
15.4 |
|
|
|
|
|
|
|
|
|
Silfuz (1/4 Hard) |
10.5 |
71 |
|
227 |
428.0 |
19.7 |
17 |
60.6 |
|
|
Silfuz (annealed) |
10.5 |
71 |
|
190 |
428.0 |
19.7 |
16 |
62.1 |
|
|
Silver |
10.5 |
71 |
54 |
125 |
418.7 |
20.6 |
1770 |
0.6 |
25 |
|
Silver-ABA® |
10.0 |
77 |
136 |
282 |
344.0 |
20.7 |
22 |
45.0 |
87 |
37 |
Sterling Silver |
|
|
124 |
207 |
|
|
|
|
|
41 |
Ticuni® |
|
|
|
|
|
|
|
|
|
|
Ticuni®-60 |
|
|
|
|
|
|
|
|
|
|
Ticusil®*** |
9.4 |
85 |
292 |
339 |
219.0 |
18.5 |
34 |
29.0 |
|
28 |
*** These properties are listed for the composite material Ticusil® and are not valid after brazing.
The determination of adaptability of any Wesgo® materials to the specific needs of the Buyer is solely the Buyer's prerogative and responsibility. All technical information, data, and recommendations are based on tests and accumulated experience, which Wesgo® believes to be reliable. However, the accuracy and completeness thereof are not guaranteed.