TiNi™-67 Technical Information
A high-purity Active Brazing Filler in composite form containing titanium, copper and nickel, developed for direct application to ceramic surfaces
Key Benefits
- Wets and bonds to virtually any metallic surface, as well as to non-metallics such as oxides, nitrides and carbides
- Allows ceramic-to-ceramic and ceramic-to-metal surfaces to be brazed without metallising, firing and electroplating
- Cuts time and costs in manufacture of ceramic/metal assemblies
- Produces strong, highly reliable and vacuum-tight brazed joints
Typical Applications
- One step bonding to ceramics
Nominal Composition by Weight
- Titanium (Ti): 70%
- Copper (Cu): 15%
- Nickel (Ni): 15%
Suggested Base Materials
- Copper, Kovar, Nickel, Tool/high speed steel, Stainless steel, Ni-super alloys, Titanium, Ceramics, Graphite, Diamond
Forms Available
Sheet Preforms
|
TiNi™-67 Thermal Properties |
||
|---|---|---|
|
°C |
°F |
|
|
Liquidus |
960 |
1760 |
|
Solidus |
910 |
1670 |
|
TiNi™-67 Physical Properties* |
||||
|---|---|---|---|---|
|
Metric |
Imperial |
|||
|
Recommended Brazing Temperatures |
960 - 1100 |
°C |
1760 - 2012 |
°F |
|
Recommended Brazing Atmospheres |
10-5 mm Hg |
|||
* Please note that all values quoted are based on test pieces and may vary according to component design. These values are not guaranteed in any way and should only be treated as indicative values. They should be used for guidance only and for no other purpose whatsoever.